| Category | Item | Value / Description |
|---|---|---|
| Physical Characteristics | Particle Size | 15 ~ 53 μm |
| Morphology | Spherical | |
| Flowability | 150S (Hall Flowmeter) | |
| Apparent Density | 1.45 g/cm³ | |
| Chemical Composition | Al (Balance) | Si (9~10%) Mg (0.2~0.45%) Cu (≤0.05%) Mn (≤0.45%) Ni (≤0.05%) Fe (≤0.55%) Ti (≤0.15%) O (≤0.15%) |
| Molding Performance | Relative Density | ≥99 % |
| Density | 2.67 g/cm³ | |
| Tensile Strength | ≥330 MPa | |
| Yield Strength | ≥245 MPa | |
| Elongation at Break | 6 % | |
| Elastic Modulus | 70 GPa | |
| Hardness | 120 HB |
> Please note: Specifications are subject to change without notice. Contact a Forgecise representative for the most current technical data.
High-Performance AlSi10Mg Aluminum Alloy Powder is specifically engineered for Selective Laser Melting (SLM) and other metal additive manufacturing processes. With a precisely controlled particle size of 15–53μm, spherical morphology, and excellent flowability (150S Hall Flow), this powder ensures superior layer uniformity, minimal porosity, and exceptional mechanical properties in as-built condition — ideal for lightweight structural components requiring high strength-to-weight ratio.
Designed for aerospace brackets, automotive engine parts, drone frames, heat exchangers, consumer electronics housings, and rapid prototyping applications. After SLM processing, parts achieve near-full density (≥99%), with tensile strength ≥330 MPa, yield strength ≥245 MPa, elongation up to 6%, and hardness of 120 HB — meeting or exceeding ASTM F3055 and EN AC-43000 specifications.
Key Advantages:
- Optimized for SLM/DMLS systems
- Low oxygen content (≤0.15%) and iron (≤0.55%) for enhanced weldability and reduced cracking
- Very low apparent density (1.45 g/cm³) enables efficient powder handling and reduced material waste
- Fully traceable chemical composition compliant with ASTM B221 / EN AC-43000 specifications
Technical Specs Summary:
- Particle Size: 15–53μm | Morphology: Spherical | Flowability: 150S
- Chemical Balance: Al + Si(9–10%) + Mg(0.2–0.45%) + Cu/Mn/Ni/Fe/Ti/O trace elements
- As-Built Properties: ≥99% density, 2.67 g/cm³, 330+ MPa UTS, 245+ MPa YS, 6% elongation, 120 HB hardness
Forgecise AlSi10Mg Aluminum Alloy Powder trusted by aerospace engineers, automotive designers, and industrial manufacturers worldwide for reliable, repeatable, high-strength aluminum 3D printing solutions.